Water Soluble Low Temperature Baking Paint Formulation Reference and High Temperature High Hardness Baking Paint Reference Formulation

customers highlight water-based low-temperature baking metal baking varnish, which only requires a certain hardness of adhesion. They are mainly used to make varnish and water-based high-temperature baking varnish. Mitsubishi pencil 4H is required to have good adhesion and certain salt spray resistance. Here, we recommend the reference formula for your reference and testing. Next, look down with the small series.

Low temperature baking metallic paint reference formula

resin 06201 40-45

amino 303 20-22

Dimethylethanolamine 3-5

adhesion promoter 6065 2.5

PM 10

DPM 4

wetting agent 1136 0.5

leveling agent 1007 0.3

Defoamer 3145 0.3-0.5

Dispersant 2019 1-2

anti-stick slip 1044 0.2-0.5

Anti-flash Rust 8066 0.2-0.8

cooling agent 8044 0.5-1.5

deionized water balance

Total 100

When spraying, the main paint is diluted with water by 1:0.2-0.4, the film thickness is 5-12 microns, pre-baked at 60-70 degrees for 3-5 minutes, and baked at 100-120 degrees for 8-15 minutes. The hardness of the paint film is 1-2H, the gloss is above 97, and the surface is smooth and flat.

high temperature baking metallic paint formula

resin 06201 40-45

amino 303 20-22

Dimethylethanolamine 3-5

adhesion promoter 6065 2.5

PM 10

DPM 4

wetting agent 1136 0.5

leveling agent 1007 0.3

Defoamer 3145 0.3-0.5

Dispersant 2019 1-2

anti-stick slip 1044 0.2-0.5

Anti-flash Rust 8066 0.2-0.8

cooling agent 8047 0.5-1.5

deionized water balance

Total 100

When spraying, the main paint is diluted with water by 1:0.2-0.4, the film thickness is 5-12 microns, pre-baked at 60-70 degrees for 3-5 minutes, and baked at 160-180 degrees for 15-30 minutes. The hardness of paint film is 2-6H, gloss is above 97, and the surface is smooth and flat.

The above are some formulas compiled by Xiao Bian. Those who are interested in baking varnish resin can contact us. We have deep attainments in the field of baking varnish resin. Welcome to consult.